- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.2
- 缺口沖擊強度: 9.0
- 拉伸強度 [MPa]: 75.0
- 彎曲模量 [MPa]: 2.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in3 | ISO 1183/A | ||
| Water Absorption | 1.2 % @Temperature 23.0 °C, Time 86400 sec | 1.2 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0142 cm/cm | 0.0142 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0132 cm/cm | 0.0132 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ISO 527 type 1 A | ||
| Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 | ||
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 9.00 kJ/m2 | 4.28 ft-lb/in2 | ISO 180/1eA | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.10 J/cm2 | 5.23 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Constant | 3.5 | 3.5 | IEC 60250 | ||
| Dissipation Factor | 0.20 | 0.20 | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 70.0 μm/m-°C @Temperature 23.0 - 85.0 °C | 38.9 μin/in-°F @Temperature 73.4 - 185 °F | ISO 11359 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75/Af | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | 1210 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 220 - 225 °C | 428 - 437 °F | |||
| Front Barrel Temperature | 225 - 230 °C | 437 - 446 °F | |||
| Melt Temperature | 222 °C | 432 °F | ISO 11357 | ||
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 225-230°C | ||||