- 密度 [g/cm3]: 1.14
- 缺口沖擊強度: 16.0
- 拉伸強度 [MPa]: 50.0
- 彎曲模量 [MPa]: 1.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 type 1 A |
| Elongation at Break | 400 % | 400 % | ISO 527 Type 1A |
| Elongation at Yield | 25 % | 25 % | ISO 527 type 1 A |
| Tensile Modulus | 1.10 GPa | 160 ksi | ISO 527 Type 1A |
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m2 | 7.61 ft-lb/in2 | ISO 180/1eA |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 1.60 J/cm2 | 7.61 ft-lb/in2 | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | IEC 60243 |
| Dissipation Factor | 0.10 | 0.10 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
| Moisture Content | <= 0.20 % | <= 0.20 % | |