- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.3
- 缺口沖擊強度: 4.5
- 彎曲模量 [MPa]: 2.90
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ISO 1183/A | ||
| Water Absorption | 1.3 % @Temperature 23.0 °C, Time 86400 sec | 1.3 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 Type 1A | ||
| Elongation at Break | 100 % | 100 % | ISO 527 Type 1A | ||
| Tensile Modulus | 2.95 GPa | 428 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 | ||
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 4.50 kJ/m2 | 2.14 ft-lb/in2 | ISO 180/1eA | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.500 J/cm2 | 2.38 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Constant | 3.4 | 3.4 | IEC 60250 | ||
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 | ||
| Comparative Tracking Index | 575 V | 575 V | Solution B; IEC 60112 | ||
| 600 V | 600 V | Solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 70.0 μm/m-°C @Temperature 23.0 - 85.0 °C | 38.9 μin/in-°F @Temperature 73.4 - 185 °F | ISO 11359 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75/Af | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | 1210 | ||
| Oxygen Index | 26 % | 26 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 220 - 230 °C | 428 - 446 °F | |||
| Front Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Melt Temperature | 222 °C | 432 °F | ISO 11357 | ||
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 225-235°C | ||||