- 密度 [g/cm3]: 1.37
- 拉伸強度 [MPa]: 35.0
- 彎曲模量 [MPa]: 2.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ISO 527 type 1 A |
| Elongation at Break | 12.2 % | 12.2 % | ISO 527 Type 1A |
| Elongation at Yield | 18.2 % | 18.2 % | ISO 527 type 1 A |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527 Type 1A |
| Flexural Strength | 56.0 MPa | 8120 psi | ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Charpy Impact Unnotched | 6.00 J/cm2 | 28.6 ft-lb/in2 | ISO 179/1eU |
| Charpy Impact, Notched | 0.580 J/cm2 | 2.76 ft-lb/in2 | ISO 179/1eA |
| Processing Properties | Metric | English | Comments |
| Moisture Content | <= 0.20 % | <= 0.20 % | |