- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 1.1
- 拉伸強度 [MPa]: 80.0
- 斷裂伸長率 [%]: 105
- 彎曲強度 [MPa]: 80.0
- 彎曲模量 [MPa]: 3.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | ISO 1183-A |
| Water Absorption | 1.1 % | 1.1 % | 24 hours in water at 23°C; ISO 62. |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ISO 527 |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 3.70 GPa | 537 ksi | ISO 527 |
| Flexural Yield Strength | 105 MPa | 15200 psi | ISO 178 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ISO 178 |
| Izod Impact Resistance | 0.300 J/cm2 | 1.43 ft-lb/in2 | ISO 180 |
| Charpy Impact Unnotched | 6.00 J/cm2 | 28.6 ft-lb/in2 | ISO 179/1EA-1993 |
| Charpy Impact, Notched | 0.300 J/cm2 | 1.43 ft-lb/in2 | ISO 179/1EA-1993 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 93 |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz | 3.6 @Frequency 1e+6 Hz | IEC 250 |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 243-1 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 μm/m-°C @Temperature 23.0 - 85.0 °C | 36.1 μin/in-°F @Temperature 73.4 - 185 °F | ASTM E831 |
| Melting Point | 242 °C | 468 °F | ISO 3146-C |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-2 |
| Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | ISO 1210/UL 94 |
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | ISO 1210/UL 94 | |
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | ISO 1210/UL 94 | |
| Oxygen Index | 37 % | 37 % | ISO 4589 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 240 - 250 °C | 464 - 482 °F | |
| Middle Barrel Temperature | 245 - 255 °C | 473 - 491 °F | |
| Front Barrel Temperature | 250 - 260 °C | 482 - 500 °F | |