- 密度 [g/cm3]: 1.13
- 拉伸強度 [MPa]: 78.0
- 熱變形溫度 [℃]: 117.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ISO 1183/A | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 Type 1A | ||
| Tensile Strength, Yield | 78.0 MPa | 11300 psi | ISO 527 type 1 A | ||
| Elongation at Break | 30 % | 30 % | ISO 527 Type 1A | ||
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 type 1 A | ||
| Tensile Modulus | 2.78 GPa | 403 ksi | ISO 527 Type 1A | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.580 J/cm2 | 2.76 ft-lb/in2 | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 117 °C | 243 °F | ISO 75/Bf | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75/Af | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 230 °C | 446 °F | |||
| Front Barrel Temperature | 230 °C | 446 °F | |||
| Die Temperature | 240 °C | 464 °F | |||
| Melt Temperature | 222 °C | 432 °F | ISO 11357 | ||
| Descriptive Properties | |||||
| Compression Zone | 230oC | ||||