- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 1.1
- 缺口沖擊強度: 0.6
- 拉伸強度 [MPa]: 80.0
- 彎曲模量 [MPa]: 3.65
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | ISO 1183/A | ||
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec | 1.1 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Viscosity | 25 cP @Shear Rate 100 1/s, Temperature 290 °C | 25 cP @Shear Rate 100 1/s, Temperature 554 °F | |||
| 27 cP @Shear Rate 1000 1/s, Temperature 290 °C | 27 cP @Shear Rate 1000 1/s, Temperature 554 °F | ||||
| 29 cP @Shear Rate 1000 1/s, Temperature 270 °C | 29 cP @Shear Rate 1000 1/s, Temperature 518 °F | ||||
| 30 cP @Shear Rate 1000 1/s, Temperature 260 °C | 30 cP @Shear Rate 1000 1/s, Temperature 500 °F | ||||
| 107 cP @Shear Rate 100 1/s, Temperature 270 °C | 107 cP @Shear Rate 100 1/s, Temperature 518 °F | ||||
| 109 cP @Shear Rate 100 1/s, Temperature 260 °C | 109 cP @Shear Rate 100 1/s, Temperature 500 °F | ||||
| 109 cP @Shear Rate 10.0 1/s, Temperature 290 °C | 109 cP @Shear Rate 10.0 1/s, Temperature 554 °F | ||||
| 120 cP @Shear Rate 10.0 1/s, Temperature 270 °C | 120 cP @Shear Rate 10.0 1/s, Temperature 518 °F | ||||
| 130 cP @Shear Rate 10.0 1/s, Temperature 260 °C | 130 cP @Shear Rate 10.0 1/s, Temperature 500 °F | ||||
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | Isotropy | ||
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 Type 1A | ||
| Tensile Stress | 35.0 MPa @Strain 1.00 % | 5080 psi @Strain 1.00 % | |||
| 62.0 MPa @Strain 2.00 % | 8990 psi @Strain 2.00 % | ||||
| 75.0 MPa @Strain 3.00 % | 10900 psi @Strain 3.00 % | ||||
| 78.0 MPa @Strain 4.00 % | 11300 psi @Strain 4.00 % | ||||
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 type 1 A | ||
| 85.0 MPa | 12300 psi | ASTM D638 | |||
| Elongation at Break | 10 % | 10 % | ASTM D638 | ||
| 10 % | 10 % | ISO 527 Type 1A | |||
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 type 1 A | ||
| Tensile Modulus | 3.60 GPa | 522 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 105 MPa | 15200 psi | ISO 178 | ||
| 120 MPa | 17400 psi | ASTM D790 | |||
| Flexural Modulus | 3.65 GPa | 529 ksi | ISO 178 | ||
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | ISO 180/1eA | ||
| Charpy Impact Unnotched | 9.00 J/cm2 | 42.8 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.450 J/cm2 | 2.14 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.6 | 3.6 | IEC 60250 | ||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243 | ||
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 | ||
| Comparative Tracking Index | 575 V | 575 V | Solution B; IEC 60112 | ||
| 600 V | 600 V | Solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 65.0 μm/m-°C @Temperature 23.0 - 85.0 °C | 36.1 μin/in-°F @Temperature 73.4 - 185 °F | ISO 11359 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75/Af | ||
| UL RTI, Electrical | 120 °C @Thickness 0.380 - 3.00 mm | 248 °F @Thickness 0.0150 - 0.118 in | |||
| UL RTI, Mechanical with Impact | 90.0 °C @Thickness 0.750 - 3.00 mm | 194 °F @Thickness 0.0295 - 0.118 in | |||
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | 1210 | ||
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | 1210 | |||
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | 1210 | |||
| V-0 @Thickness 0.380 mm | V-0 @Thickness 0.0150 in | 1210 | |||
| Oxygen Index | 33 % | 33 % | ISO 4589 | ||
| Glow Wire Test | 650 °C @Thickness 1.60 mm | 1200 °F @Thickness 0.0630 in | ignition temperature; ISO 60695-2-13 | ||
| 960 °C @Thickness 0.800 mm | 1760 °F @Thickness 0.0315 in | ISO 60695-2-12 | |||
| 960 °C @Thickness 1.60 mm | 1760 °F @Thickness 0.0630 in | ISO 60695-2-12 | |||
| 960 °C @Thickness 3.20 mm | 1760 °F @Thickness 0.126 in | ISO 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 240 - 250 °C | 464 - 482 °F | |||
| Front Barrel Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 242 °C | 468 °F | ISO 11357 | ||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 245-255°C | ||||
| Fire and smoke F index | I2/F3 | NF F 16 101 | |||