- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 1.1
- 缺口沖擊強(qiáng)度: 4.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in3 | ISO 1183/A | ||
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec | 1.1 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm | 0.0065 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0085 cm/cm | 0.0085 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 Type 1A | ||
| Elongation at Break | 2.7 % | 2.7 % | ISO 527 Type 1A | ||
| Tensile Modulus | 6.85 GPa | 994 ksi | ISO 527 Type 1A | ||
| Izod Impact, Notched (ISO) | 4.70 kJ/m2 | 2.24 ft-lb/in2 | ISO 180/1eA | ||
| Charpy Impact Unnotched | 4.10 J/cm2 | 19.5 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.350 J/cm2 | 1.67 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 550 V | 550 V | Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75/Af | ||
| Flammability, UL94 | V-2 @Thickness 0.800 mm | V-2 @Thickness 0.0315 in | 1210 | ||
| V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | 1210 | |||
| Glow Wire Test | 960 °C @Thickness 0.800 mm | 1760 °F @Thickness 0.0315 in | ISO 60695-2-12 | ||
| 960 °C @Thickness 1.60 mm | 1760 °F @Thickness 0.0630 in | ISO 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Front Barrel Temperature | 240 - 250 °C | 464 - 482 °F | |||
| Melt Temperature | 220 °C | 428 °F | ISO 11357 | ||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 235-245°C | ||||