- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.36
- 彎曲模量 [MPa]: 8.75
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | STN 64 0111 |
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | STN 64 0808 |
| Linear Mold Shrinkage, Transverse | 0.0112 cm/cm | 0.0112 in/in | STN 64 0808 |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 446 °F | STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 175 MPa | 25400 psi | STN EN ISO 527-2 |
| Elongation at Break | 4.0 % | 4.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 9.50 GPa | 1380 ksi | STN EN ISO 527-2 |
| Flexural Strength | 220 MPa | 31900 psi | STN EN ISO 178 |
| Flexural Modulus | 8.75 GPa | 1270 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 7.00 J/cm2 @Temperature -20.0 °C | 33.3 ft-lb/in2 @Temperature -4.00 °F | STN EN ISO 179 |
| 7.50 J/cm2 @Temperature 23.0 °C | 35.7 ft-lb/in2 @Temperature 73.4 °F | STN EN ISO 179 | |
| Charpy Impact, Notched | 1.00 J/cm2 @Temperature -20.0 °C | 4.76 ft-lb/in2 @Temperature -4.00 °F | STN EN ISO 179 |
| 1.20 J/cm2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | STN EN ISO 179 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 245 °C | 473 °F | DSC; STN EN ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | STN EN ISO 75/A |
| Vicat Softening Point | 250 °C | 482 °F | B; STN EN ISO 306 |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | STN IEC 60695-2-10 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.15 % | 0.15 % | STN EN ISO 960 |
| Injection Pressure | 70.0 - 120 MPa | 10200 - 17400 psi | |