- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 1.5
- 缺口沖擊強度: 2.5
- 拉伸強度 [MPa]: 80.0
- 斷裂伸長率 [%]: 110
- 彎曲模量 [MPa]: 3.00
- 熱變形溫度 [℃]: 207.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in3 | ASTM D792, ISO 1183 | ||
| Water Absorption | 1.5 % | 1.5 % | 23°C, 24h in H2O; sim. ISO 62 | ||
| Water Absorption at Saturation | 7.5 % | 7.5 % | sim. ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | parallel; Euronil | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | Euronil | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527, ASTM D638 | ||
| Elongation at Break | 5.0 % | 5.0 % | |||
| Tensile Modulus | 3.60 GPa | 522 ksi | ISO 527, ASTM D638 | ||
| Flexural Yield Strength | 110 MPa | 16000 psi | ISO 178, ASTM D790 | ||
| 30.0 MPa @Temperature 90.0 °C | 4350 psi @Temperature 194 °F | ISO 178, ASTM D790 | |||
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178, ASTM D790 | ||
| 0.850 GPa @Temperature 90.0 °C | 123 ksi @Temperature 194 °F | ISO 178, ASTM D790 | |||
| Izod Impact, Notched (ISO) | 2.50 kJ/m2 @Temperature -30.0 °C | 1.19 ft-lb/in2 @Temperature -22.0 °F | ISO 180/1A | ||
| 3.50 kJ/m2 @Temperature 23.0 °C | 1.67 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | 4.50 J/cm2 | 21.4 ft-lb/in2 | ISO 179 | ||
| 3.60 J/cm2 @Temperature -30.0 °C | 17.1 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 0.450 J/cm2 | 2.14 ft-lb/in2 | ISO 179 | ||
| 0.350 J/cm2 @Temperature -30.0 °C | 1.67 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 18.0 kV/mm @Thickness 2.00 mm | 457 kV/in @Thickness 0.0787 in | ASTM D149 | ||
| Comparative Tracking Index | >= 600 V @Thickness 3.20 mm | >= 600 V @Thickness 0.126 in | Sol. B; IEC 112, UL 746A | ||
| >= 600 V @Thickness 3.20 mm | >= 600 V @Thickness 0.126 in | Sol. A; IEC 112, UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 120 °C | 248 °F | 20,000 hr; IEC 216 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C | 405 °F | ISO 75, ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75, ASTM D648 | ||
| Vicat Softening Point | 220 °C | 428 °F | 49 N; ISO 306, ASTM D1525 | ||
| 235 °C | 455 °F | 9.8 N; ISO 306, ASTM D1525 | |||
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |||
| V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | ||||
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | ||||
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||||
| Oxygen Index | 28 % | 28 % | ASTM D2863 | ||
| Glow Wire Test | 960 °C @Thickness 0.800 mm | 1760 °F @Thickness 0.0315 in | Glow Wire Flammability Index; IEC 694-2-12 | ||
| 960 °C @Thickness 3.20 mm | 1760 °F @Thickness 0.126 in | Glow Wire Flammability Index; IEC 694-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | |||
| Zone 1 | 260 - 270 °C | 500 - 518 °F | hopper | ||
| Zone 2 | 260 - 275 °C | 500 - 527 °F | |||
| Zone 3 | 270 - 280 °C | 518 - 536 °F | |||
| Zone 4 | 270 - 280 °C | 518 - 536 °F | |||
| Melt Temperature | 265 - 280 °C | 509 - 536 °F | Do not melt above 280°C | ||
| Mold Temperature | >= 80.0 °C | >= 176 °F | |||
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi | |||
| Descriptive Properties | |||||
| Clamping Force | in tons, 0.7 times the projected surface area in cm2 | ||||
| Flammability Rating | SE | FMVSS No. 302, 355x100x1 mm | |||
| Heat Resistance - Ball Test | OK | at 125°C, IEC 309 | |||
| OK | at 165°C, IEC 309 | ||||
| Holding Pressure | 90 MPa | ||||
| Needle Test | OK | IEC 695-2-2, 1 or 2 mm | |||