- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 1.3
- 彎曲模量 [MPa]: 12.0
- 熱變形溫度 [℃]: 245.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc @Temperature 23.0 °C | 0.0535 lb/in3 @Temperature 73.4 °F | ISO 1183 | ||
| Filler Content | 40 % | 40 % | ISO 1172 | ||
| Water Absorption | 1.3 % @Temperature 23.0 °C | 1.3 % @Temperature 73.4 °F | 50% r.h.; ISO 62 | ||
| Water Absorption at Saturation | 4.0 - 4.5 % | 4.0 - 4.5 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | <= 0.0010 cm/cm | <= 0.0010 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 | ||
| Spiral Flow | 664 cm | 261 in | Akro | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 230 MPa | 33400 psi | 5 [mm/min]; ISO 527-1/2 | ||
| 115 MPa @Temperature 140 - 150 °C, Time 1.80e+7 sec | 16700 psi @Temperature 284 - 302 °F, Time 5000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |||
| 115 MPa @Temperature 110 - 130 °C, Time 7.20e+7 sec | 16700 psi @Temperature 230 - 266 °F, Time 20000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |||
| Elongation at Break | 3.0 % | 3.0 % | 5 [mm/min]; ISO 527-1/2 | ||
| Tensile Modulus | 13.0 GPa | 1890 ksi | 1[mm/min]; ISO 527-1/2 | ||
| Flexural Strength | 325 MPa | 47100 psi | 2 [mm/min]; ISO 178 | ||
| Flexural Modulus | 12.0 GPa | 1740 ksi | 2 [mm/min]; ISO 178 | ||
| Charpy Impact Unnotched | 8.00 J/cm2 @Temperature -30.0 °C | 38.1 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 9.50 J/cm2 @Temperature 23.0 °C | 45.2 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm2 @Temperature -30.0 °C | 6.19 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.40 J/cm2 @Temperature 23.0 °C | 6.66 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 15.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 8.33 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/2 | ||
| CTE, linear, Transverse to Flow | 70.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 38.9 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/2 | ||
| Melting Point | 255 °C | 491 °F | ISO 11357-1, DSC,10 [K/min] | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | HDT/B; ISO 75-1/2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | HDT/A; ISO 75-1/2 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 80.0 °C | 176 °F | |||
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |||
| Zone 1 | 275 - 305 °C | 527 - 581 °F | |||
| Zone 2 | 275 - 305 °C | 527 - 581 °F | |||
| Zone 3 | 275 - 305 °C | 527 - 581 °F | |||
| Zone 4 | 275 - 305 °C | 527 - 581 °F | |||
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 - 8 hour | 4 - 8 hour | |||
| Injection Pressure | 100 MPa | 14500 psi | |||
| Hold Pressure | 30.0 - 80.0 MPa | 4350 - 11600 psi | |||
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi | |||
| Descriptive Properties | |||||
| Rate acc. FMVSS 302 (<100/min) | Passed | ||||
| Rate acc. FMVSS 302,(<100/min) | FMVSS 302, >1 [mm] Thickness | ||||