- 密度 [g/cm3]: 2.24
- 缺口沖擊強度: 1.1
- 拉伸強度 [MPa]: 16.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.24 g/cc | 0.0809 lb/in3 | ISO 1183 |
| Filler Content | 25 % | 25 % | Glass Fibers |
| Particle Size | 40 μm | 40 μm | Average |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ISO 868 |
| Ball Indentation Hardness | 38.0 MPa | 5510 psi | ISO 2039-1 |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | ISO 527 |
| Elongation at Break | 260 % | 260 % | ISO 527 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ISO 180 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.90e+13 ohm | 1.90e+13 ohm | IEC 60093 |
| Dielectric Constant | 2.1 | 2.1 | IEC 60250 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.42 | 0.42 | IEC 60250 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 μm/m-°C @Temperature 20.0 °C | 36.1 μin/in-°F @Temperature 68.0 °F | ASTM E 831 |
| Melting Point | 327 °C | 621 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 370 °C | 698 °F | Molding |
| Back Pressure | 50.0 - 70.0 MPa | 7250 - 10200 psi | Molding Pressure |