- 密度 [g/cm3]: 2.16
- 缺口沖擊強度: 2.0
- 拉伸強度 [MPa]: 13.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.16 g/cc | 0.0780 lb/in3 | ISO 1183 |
| Filler Content | 20 % | 20 % | Graphite |
| Particle Size | 40 μm | 40 μm | Average |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ISO 868 |
| Ball Indentation Hardness | 53.0 MPa | 7690 psi | ISO 2039-1 |
| Tensile Strength, Yield | 13.0 MPa | 1890 psi | ISO 527 |
| Elongation at Break | 140 % | 140 % | ISO 527 |
| Izod Impact, Notched | 2.00 J/cm | 3.75 ft-lb/in | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 μm/m-°C @Temperature 20.0 °C | 36.1 μin/in-°F @Temperature 68.0 °F | ASTM E 831 |
| Melting Point | 327 °C | 621 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 370 °C | 698 °F | Molding |
| Back Pressure | 40.0 - 60.0 MPa | 5800 - 8700 psi | Molding Pressure |