- 密度 [g/cm3]: 2.21
- 缺口沖擊強度: 1.2
- 拉伸強度 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.21 g/cc | 0.0798 lb/in3 | ISO 1183 |
| Particle Size | 40 μm | 40 μm | Average |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58 | 58 | ISO 868 |
| Ball Indentation Hardness | 39.0 MPa | 5660 psi | ISO 2039-1 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO 527 |
| Elongation at Break | 260 % | 260 % | ISO 527 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ISO 180 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 2.00e+13 ohm | 2.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 7.0 | 7.0 | IEC 60250 |
| Dielectric Strength | 7.00 kV/mm | 178 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.30 | 0.30 | IEC 60250 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 μm/m-°C @Temperature 20.0 °C | 36.1 μin/in-°F @Temperature 68.0 °F | ASTM E 831 |
| Melting Point | 327 °C | 621 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 370 °C | 698 °F | Molding |
| Back Pressure | 35.0 - 40.0 MPa | 5080 - 5800 psi | Molding Pressure |