- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.78
- 缺口沖擊強度: 0.6
- 斷裂伸長率 [%]: 170
- 彎曲強度 [MPa]: 80.0
- 彎曲模量 [MPa]: 7.50
- 熱變形溫度 [℃]: 170.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in3 | ISO 1183 |
| Water Absorption | <= 0.050 % | <= 0.050 % | ISO 62 (method 1) |
| Linear Mold Shrinkage | <= 0.010 cm/cm | <= 0.010 in/in | |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| 9.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 9.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 82 @Thickness 2.00 mm | 82 @Thickness 0.0787 in | ASTM D2240 |
| Tensile Strength, Ultimate | 80.0 - 120 MPa | 11600 - 17400 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 1.0 - 4.0 % | 1.0 - 4.0 % | 50 mm/min; ASTM D638 |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | 1 mm/min; ASTM D638 |
| Flexural Yield Strength | 170 MPa | 24700 psi | 2 mm/min; ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | 2 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm @Thickness 4.00 mm, Temperature 23.0 °C | 1.12 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F | Notched V 10 mm; ASTM D256 |
| Coefficient of Friction | 0.20 - 0.30 | 0.20 - 0.30 | ASTM D1894 |
| Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | ASTM D1894 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | Intensity = 10 mA after 2 min @ 23°C; ASTM D 257; DIN 53483 |
| Thermal Properties | Metric | English | Comments |
| Heat of Fusion | 59.0 J/g | 25.4 BTU/lb | Crystallization Heat |
| 67.0 J/g | 28.8 BTU/lb | 80°C to end of melting | |
| CTE, linear | 70.0 - 90.0 μm/m-°C @Temperature 20.0 °C | 38.9 - 50.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft2-°F | ASTM C177 |
| Melting Point | 174 °C | 345 °F | Crystallinity by DSC; ASTM D 3418 |
| Crystallization Temperature | 140 °C | 284 °F | |
| Maximum Service Temperature, Air | 330 - 400 °C | 626 - 752 °F | Thermal Stability via TGA : beginning - and at 1% weight loss in air |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C @Thickness 4.00 mm | 338 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C @Thickness 4.00 mm | 316 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| Vicat Softening Point | 172 °C @Load 1.00 kg, Thickness 4.00 mm | 342 °F @Load 2.20 lb, Thickness 0.157 in | ISO 306 |
| Brittleness Temperature | >= 0.000 °C | >= 32.0 °F | ASTM D746A |
| Glass Transition Temp, Tg | -35.0 °C | -31.0 °F | DMTA |
| Flammability, UL94 | V-0 | V-0 | |