- 吸水率 [%]: 0.04
- 拉伸強度 [MPa]: 11.7
- 彎曲強度 [MPa]: 27.6
- 彎曲模量 [MPa]: 0.193
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.80 - 1.82 g/cc | 1.80 - 1.82 g/cc | ASTM D792 |
| Water Absorption | 0.040 - 0.070 % | 0.040 - 0.070 % | 24 hr / 20°C; ASTM D570 |
| Viscosity | 8.00e+6 cP @Shear Rate 100 1/s, Temperature 232 °C | 8.00e+6 cP @Shear Rate 100 1/s, Temperature 450 °F | ASTM D3835 |
| Ash | 0.00 - 5.0 % | 0.00 - 5.0 % | Thermal Decomposition/ in air |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 55 - 60 | 55 - 60 | ASTM D2240 |
| Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | ASTM D638 |
| Tensile Strength, Yield | 11.7 - 19.3 MPa | 1700 - 2800 psi | ASTM D638 |
| Elongation at Break | 500 - 800 % | 500 - 800 % | ASTM D638 |
| Elongation at Yield | 12 - 25 % | 12 - 25 % | ASTM D638 |
| Tensile Modulus | 0.241 - 0.379 GPa | 35.0 - 55.0 ksi | ASTM D638 |
| Flexural Strength | 10.3 - 17.2 MPa | 1500 - 2500 psi | @ 5% strain; ASTM D790 |
| Flexural Modulus | 0.193 - 0.248 GPa | 28.0 - 36.0 ksi | ASTM D790 |
| Compressive Strength | 13.8 - 20.7 MPa | 2000 - 3000 psi | ASTM D695 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.54 | 0.54 | vs. Steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.49 | 0.49 | vs. Steel; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 28 - 33 | 28 - 33 | CS-17 1000g:load |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | DC, 65% RH; ASTM D257 |
| Dielectric Constant | 4.5 - 5.8 @Frequency 1e+8 Hz | 4.5 - 5.8 @Frequency 1e+8 Hz | ASTM D150 |
| 10.9 - 13.5 @Frequency 100 Hz | 10.9 - 13.5 @Frequency 100 Hz | ASTM D150 | |
| Dielectric Strength | 31.5 - 43.3 kV/mm | 800 - 1100 kV/in | ASTM D149 |
| Dissipation Factor | 0.060 - 0.10 @Frequency 100 Hz | 0.060 - 0.10 @Frequency 100 Hz | ASTM D150 |
| 0.25 - 0.29 @Frequency 1e+8 Hz | 0.25 - 0.29 @Frequency 1e+8 Hz | ASTM D150 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 153 - 194 μm/m-°C @Temperature 20.0 °C | 85.0 - 108 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.17 - 1.51 J/g-°C | 0.280 - 0.360 BTU/lb-°F | DSC |
| Thermal Conductivity | 0.144 - 0.180 W/m-K | 1.00 - 1.25 BTU-in/hr-ft2-°F | ASTM D433 |
| Deflection Temperature at 1.8 MPa (264 psi) | 26.7 - 37.8 °C | 80.0 - 100 °F | ASTM D648 |
| Glass Transition Temp, Tg | -46.0 - -40.0 °C | -50.8 - -40.0 °F | (DMA) @ 1 Hz |
| Decomposition Temperature | 375 °C | 707 °F | 1% wt. loss / in air |
| 410 °C | 770 °F | 1% wt. loss / in nitrogen | |
| Oxygen Index | 42 % | 42 % | Limiting, (Optional product available with higher value of 95% O2; ASTM D2868 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.40 @Temperature 25.0 °C, Wavelength 589.3 nm | 1.40 @Temperature 77.0 °F, Wavelength 589.3 nm | Sodium D line; ASTM D542 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 116 - 121 °C | 240 - 250 °F | ASTM D3418 |