- 熔體流動速率 [g/10min]: 2.0
- 吸水率 [%]: 0.03
- 拉伸強度 [MPa]: 24.1
- 彎曲強度 [MPa]: 34.5
- 彎曲模量 [MPa]: 0.621
- 熱變形溫度 [℃]: 54.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.76 - 1.79 g/cc | 1.76 - 1.79 g/cc | ASTM D792 |
| Water Absorption | 0.030 - 0.050 % | 0.030 - 0.050 % | 24 hr / 20°C; ASTM D570 |
| Viscosity | 2.00e+7 cP @Shear Rate 100 1/s, Temperature 232 °C | 2.00e+7 cP @Shear Rate 100 1/s, Temperature 450 °F | ASTM D3835 |
| Melt Flow | 2.0 g/10 min @Load 12.5 kg, Temperature 232 °C | 2.0 g/10 min @Load 27.6 lb, Temperature 450 °F | ASTM D1238 |
| Ash | 0.00 - 5.0 % | 0.00 - 5.0 % | Thermal Decomposition/ in air |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 - 70 | 65 - 70 | ASTM D2240 |
| Tensile Strength, Ultimate | 34.5 - 48.3 MPa | 5000 - 7000 psi | ASTM D638 |
| Tensile Strength, Yield | 24.1 - 34.5 MPa | 3500 - 5000 psi | ASTM D638 |
| Elongation at Break | 300 - 550 % | 300 - 550 % | ASTM D638 |
| Elongation at Yield | 10 - 20 % | 10 - 20 % | ASTM D638 |
| Tensile Modulus | 0.552 - 0.896 GPa | 80.0 - 130 ksi | ASTM D638 |
| Flexural Strength | 20.7 - 34.5 MPa | 3000 - 5000 psi | @ 5% strain; ASTM D790 |
| Flexural Modulus | 0.621 - 0.827 GPa | 90.0 - 120 ksi | ASTM D790 |
| Compressive Strength | 31.0 - 41.4 MPa | 4500 - 6000 psi | ASTM D695 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | vs. Steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.31 | 0.31 | vs. Steel; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | 1kg, CS 17; ISO 9352 |
| 16 - 19 | 16 - 19 | CS-17 1000g:load | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | DC, 65% RH; ASTM D257 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.2 - 3.9 @Frequency 1e+8 Hz | 3.2 - 3.9 @Frequency 1e+8 Hz | ASTM D150 |
| 8.7 - 10.2 @Frequency 100 Hz | 8.7 - 10.2 @Frequency 100 Hz | ASTM D150 | |
| Dielectric Strength | 51.2 - 59.1 kV/mm | 1300 - 1500 kV/in | ASTM D149 |
| Dissipation Factor | 0.080 - 0.14 @Frequency 100 Hz | 0.080 - 0.14 @Frequency 100 Hz | ASTM D150 |
| 0.18 - 0.19 @Frequency 1e+8 Hz | 0.18 - 0.19 @Frequency 1e+8 Hz | ASTM D150 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 126 - 185 μm/m-°C @Temperature 20.0 °C | 70.0 - 103 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.17 - 1.51 J/g-°C | 0.280 - 0.360 BTU/lb-°F | DSC |
| Thermal Conductivity | 0.144 - 0.180 W/m-K | 1.00 - 1.25 BTU-in/hr-ft2-°F | ASTM D433 |
| Deflection Temperature at 0.46 MPa (66 psi) | 54.4 - 76.7 °C | 130 - 170 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.3 - 54.4 °C | 110 - 130 °F | ASTM D648 |
| Vicat Softening Point | 85.0 °C | 185 °F | ISO 306 |
| Glass Transition Temp, Tg | -42.0 - -39.0 °C | -43.6 - -38.2 °F | (DMA) @ 1 Hz |
| Decomposition Temperature | 375 °C | 707 °F | 1% wt. loss / in air |
| 410 °C | 770 °F | 1% wt. loss / in nitrogen | |
| Oxygen Index | 42 % | 42 % | Limiting, (Optional product available with higher value of 95% O2; ASTM D2868 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.41 @Temperature 25.0 °C, Wavelength 589.3 nm | 1.41 @Temperature 77.0 °F, Wavelength 589.3 nm | Sodium D line; ASTM D542 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 163 - 166 °C | 325 - 331 °F | ASTM D3418 |