- 熔體流動速率 [g/10min]: 2.8
- 密度 [g/cm3]: 1.77
- 吸水率 [%]: 0.03
- 拉伸強度 [MPa]: 24.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in3 | |
| Water Absorption | 0.030 % | 0.030 % | |
| Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 230 °C | 2.8 g/10 min @Load 11.0 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 12 % | 12 % | 50 mm/min |
| Tensile Modulus | 0.680 GPa | 98.6 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 6.0 @Frequency 1e+6 Hz | 6.0 @Frequency 1e+6 Hz | |
| Dissipation Factor | 0.057 @Frequency 100 Hz | 0.057 @Frequency 100 Hz | |
| 0.234 @Frequency 1e+6 Hz | 0.234 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 160 μm/m-°C @Temperature 20.0 °C | 88.9 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 142 °C | 288 °F | 10°C/min |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | |
| Vicat Softening Point | 76.0 °C | 169 °F | 50°C/hr; 50N |
| Glass Transition Temp, Tg | -36.0 °C | -32.8 °F | 10°C/min |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | ||
| Oxygen Index | 42 % | 42 % | |