- 密度 [g/cm3]: 2.22
- 缺口沖擊強度: 5.66
- 拉伸強度 [MPa]: 13.0
- 彎曲模量 [MPa]: 0.600
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.22 g/cc | 0.0802 lb/in3 | ISO 1183 |
| 2.23 g/cc | 0.0806 lb/in3 | ASTM D792 | |
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0389 cm/cm @Time 86400 sec | 0.0389 in/in @Time 24.0 hour | ISO 294 |
| 0.039 cm/cm @Time 86400 sec | 0.039 in/in @Time 24.0 hour | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0449 cm/cm @Time 86400 sec | 0.0449 in/in @Time 24.0 hour | ISO 294 |
| 0.045 cm/cm @Time 86400 sec | 0.045 in/in @Time 24.0 hour | ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 13.0 MPa | 1890 psi | ASTM D638 |
| 14.0 MPa | 2030 psi | ISO 527 | |
| Elongation at Yield | 7.2 % | 7.2 % | ISO 527 |
| 9.3 % | 9.3 % | ASTM D638 | |
| Flexural Strength | 13.0 MPa | 1890 psi | ASTM D790 |
| 16.0 MPa | 2320 psi | ISO 178 | |
| Flexural Modulus | 0.600 GPa | 87.0 ksi | ISO 178 |
| 0.620 GPa | 89.9 ksi | ASTM D790 | |
| Izod Impact, Notched | 5.66 J/cm | 10.6 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 64.0 kJ/m2 | 30.5 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 30.0 J | 22.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 46.0 J | 33.9 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 121 μm/m-°C @Temperature -40.0 - 40.0 °C | 67.2 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 121 μm/m-°C @Temperature -40.0 - 40.0 °C | 67.2 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 126 μm/m-°C @Temperature -40.0 - 40.0 °C | 70.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 128 μm/m-°C @Temperature -40.0 - 40.0 °C | 71.1 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 53.0 °C @Thickness 3.20 mm | 127 °F @Thickness 0.126 in | unannealed; ASTM D648 | |