- 密度 [g/cm3]: 2.17
- 缺口沖擊強度: 6.83
- 拉伸強度 [MPa]: 14.0
- 斷裂伸長率 [%]: 20.0
- 彎曲模量 [MPa]: 0.790
- 熱變形溫度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.17 g/cc | 2.17 g/cc | ASTM D792 |
| Density | 2.17 g/cc | 0.0784 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | Type I, 5 mm/min; ASTM D638 |
| 13.0 MPa | 1890 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | 5 mm/min; ISO 527 |
| 14.0 MPa | 2030 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 9.3 % | 9.3 % | 5 mm/min; ISO 527 |
| 9.3 % | 9.3 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.5 % | 5.5 % | Type I, 5 mm/min; ASTM D638 |
| 6.1 % | 6.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 0.930 GPa | 135 ksi | 1 mm/min; ISO 527 |
| 1.01 GPa | 146 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 19.0 MPa | 2760 psi | ISO 178 |
| Flexural Yield Strength | 20.0 MPa | 2900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 0.790 GPa | 115 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 0.870 GPa | 126 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 6.83 J/cm | 12.8 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.81 J/cm | 18.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 31.0 kJ/m2 | 14.8 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 84.0 kJ/m2 | 40.0 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 79.0 °C @Thickness 3.20 mm | 174 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 57.0 °C @Thickness 3.20 mm | 135 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL 94 by SABIC-IP |