- 拉伸強(qiáng)度 [MPa]: 30.0
- 硬度: 90.0
- 熱變形溫度 [℃]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.68 g/cc | 1.68 g/cc | ISO 1183 | ||
| Water Absorption | <= 0.010 % | <= 0.010 % | ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 90 | 90 | |||
| Hardness, Shore D | 85 | 85 | DIN 53505 | ||
| Tensile Strength at Break | 54.0 MPa | 7830 psi | ISO 527 | ||
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO 527 | ||
| Elongation at Break | 250 % | 250 % | ISO 527 | ||
| Modulus of Elasticity | 1.69 GPa | 245 ksi | ISO 527 | ||
| Flexural Strength | 49.0 MPa | 7110 psi | 3.5%; ISO 178 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | NB | NB | ISO 179 | ||
| Coefficient of Friction | 0.30 | 0.30 | DIN 53375 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | VDE 0303 | ||
| Surface Resistivity per Square | >= 1.00e+12 ohm | >= 1.00e+12 ohm | VDE 0303 | ||
| Dielectric Constant | 2.6 @Frequency 1.00e+6 Hz | 2.6 @Frequency 1.00e+6 Hz | DIN 53483 | ||
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | VDE 0303 | ||
| Comparative Tracking Index | >= 600 V | >= 600 V | CTI; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 80.0 μm/m-°C @Temperature 20.0 °C | 44.4 μin/in-°F @Temperature 68.0 °F | DIN 53752 | ||
| Thermal Conductivity | 0.150 W/m-K | 1.04 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ISO 75 | ||
| Minimum Service Temperature, Air | -76.0 °C | -105 °F | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Descriptive Properties | |||||
| Acid Resistance | limited | ||||
| Aromatic Resistance | yes | ||||
| Bondability | limited | ||||
| CKW Resistance | yes | ||||
| Color | Natural | ||||
| Hydrocarbonate Resistance | yes | ||||
| Hydroxide Resistance | yes | ||||
| Ketone Resistance | yes | ||||
| Physiological indifference according | yes | ||||
| Resistance Against Hot Water | yes | ||||
| UV Stabilization | yes | ||||