- 密度 [g/cm3]: 1.8
- 缺口沖擊強度: 4.88
- 彎曲模量 [MPa]: 4.76
- 熱變形溫度 [℃]: 239.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | ASTM D792 |
| Density | 1.80 g/cc | 0.0650 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Time 86400 sec | 0.0060 - 0.0080 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 67.0 MPa | 9720 psi | 5 mm/min; ISO 527 |
| 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 6.2 % | 6.2 % | 5 mm/min; ISO 527 |
| 6.5 % | 6.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.00 GPa | 725 ksi | 1 mm/min; ISO 527 |
| 6.44 GPa | 934 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 89.0 MPa | 12900 psi | ISO 178 |
| Flexural Modulus | 4.76 GPa | 690 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.98 GPa | 722 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 4.88 J/cm | 9.14 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.4 J/cm | 25.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 45.0 kJ/m2 | 21.4 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 92.0 kJ/m2 | 43.8 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 20.0 J @Temperature 23.0 °C | 14.8 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 8.00 J | 5.90 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 24.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 13.3 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 94.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 52.2 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 239 °C | 462 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 251 °C @Thickness 3.20 mm | 484 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 198 °C @Thickness 3.20 mm | 388 °F @Thickness 0.126 in | unannealed; ASTM D648 | |