- 密度 [g/cm3]: 1.84
- 缺口沖擊強度: 5.51
- 拉伸強度 [MPa]: 52.0
- 彎曲模量 [MPa]: 3.78
- 熱變形溫度 [℃]: 219.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | ASTM D792 |
| Density | 1.84 g/cc | 0.0665 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 23°C / 50% RH; ISO 62 |
| 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec | >= 0.020 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec | 0.020 - 0.040 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
| 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 |
| 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 9.8 % | 9.8 % | 5 mm/min; ISO 527 |
| 10.7 % | 10.7 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 9.1 % | 9.1 % | 5 mm/min; ISO 527 |
| 9.4 % | 9.4 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| 4.86 GPa | 705 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 72.0 MPa | 10400 psi | ISO 178 |
| Flexural Modulus | 3.78 GPa | 548 ksi | 2 mm/min; ISO 178 |
| 4.02 GPa | 583 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 5.51 J/cm | 10.3 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.6 J/cm | 27.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 45.0 kJ/m2 | 21.4 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 96.0 kJ/m2 | 45.7 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 21.0 J @Temperature 23.0 °C | 15.5 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 10.0 J | 7.38 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 59.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 32.8 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 76.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 42.2 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 240 °C @Thickness 3.20 mm | 464 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C @Thickness 3.20 mm | 270 °F @Thickness 0.126 in | unannealed; ASTM D648 | |