- 熔體流動速率 [g/10min]: 7.0
- 吸水率 [%]: 0.007
- 拉伸強度 [MPa]: 4.83
- 彎曲強度 [MPa]: 45.0
- 彎曲模量 [MPa]: 1.20
- 熱變形溫度 [℃]: 81.0
- 透光率 [%]: 94.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 | ||
| Water Absorption | 0.0070 % | 0.0070 % | 24 hours; ASTM D570 | ||
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D3159 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 67 | 67 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D3159 | ||
| 3.45 MPa @Temperature 200 °C | 500 psi @Temperature 392 °F | ASTM D1708 | |||
| Tensile Strength, Yield | 4.83 MPa @Temperature 180 °C | 701 psi @Temperature 356 °F | ASTM D1708 | ||
| Elongation at Break | 300 % | 300 % | ASTM D3159 | ||
| 400 % @Temperature 180 °C | 400 % @Temperature 356 °F | ASTM D1708 | |||
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM D790 | ||
| Compressive Strength | 17.0 MPa | 2470 psi | ASTM D695 | ||
| Fatigue Strength | 12.0 MPa @# of Cycles 1.00e+6 | 1740 psi @# of Cycles 1.00e+6 | |||
| Izod Impact, Notched | NB | NB | ASTM D256 | ||
| NB @Temperature -60.0 °C | NB @Temperature -76.0 °F | ||||
| NB @Temperature 121 °C | NB @Temperature 250 °F | ||||
| NB @Temperature 204 °C | NB @Temperature 399 °F | ||||
| Coefficient of Friction | 0.30 - 0.40 | 0.30 - 0.40 | ASTM D1894 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | ASTM D257 | ||
| Surface Resistivity per Square | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D257 | ||
| Dielectric Constant | 2.28 @Frequency 1.36e+10 Hz | 2.28 @Frequency 1.36e+10 Hz | ASTM D1531 | ||
| 2.31 @Frequency 3.00e+9 Hz | 2.31 @Frequency 3.00e+9 Hz | ASTM D1531 | |||
| 2.33 @Frequency 1.00e+9 Hz | 2.33 @Frequency 1.00e+9 Hz | ASTM D1531 | |||
| 2.44 @Frequency 1.00e+8 Hz | 2.44 @Frequency 1.00e+8 Hz | ASTM D1531 | |||
| 2.5 - 2.6 @Frequency 1e+6 Hz | 2.5 - 2.6 @Frequency 1e+6 Hz | ASTM D1531 | |||
| 2.6 @Frequency 1000 Hz | 2.6 @Frequency 1000 Hz | ASTM D1531 | |||
| 2.6 @Frequency 10000 Hz | 2.6 @Frequency 10000 Hz | ASTM D1531 | |||
| 2.6 @Frequency 100000 Hz | 2.6 @Frequency 100000 Hz | ASTM D1531 | |||
| Dielectric Strength | 15.0 kV/mm @Thickness 3.20 mm | 381 kV/in @Thickness 0.126 in | ASTM D149 | ||
| 70.0 kV/mm @Thickness 0.250 mm | 1780 kV/in @Thickness 0.00984 in | ASTM D149 | |||
| Dissipation Factor | 0.00070 @Frequency 1000 Hz | 0.00070 @Frequency 1000 Hz | ASTM D1531 | ||
| 0.0011 @Frequency 10000 Hz | 0.0011 @Frequency 10000 Hz | ASTM D1531 | |||
| 0.0023 @Frequency 100000 Hz | 0.0023 @Frequency 100000 Hz | ASTM D1531 | |||
| 0.00308 @Frequency 1e+6 Hz | 0.00308 @Frequency 1e+6 Hz | ASTM D1531 | |||
| 0.0073 @Frequency 1.36e+10 Hz | 0.0073 @Frequency 1.36e+10 Hz | ASTM D1531 | |||
| 0.0119 @Frequency 3.00e+9 Hz | 0.0119 @Frequency 3.00e+9 Hz | ASTM D1531 | |||
| 0.0172 @Frequency 1.00e+9 Hz | 0.0172 @Frequency 1.00e+9 Hz | ASTM D1531 | |||
| 0.023 @Frequency 1.00e+8 Hz | 0.023 @Frequency 1.00e+8 Hz | ASTM D1531 | |||
| Arc Resistance | 122 sec | 122 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 50.7 J/g | 21.8 BTU/lb | DSC; ASTM D3417 | ||
| CTE, linear | 131 μm/m-°C @Temperature 0.000 - 100 °C | 72.8 μin/in-°F @Temperature 32.0 - 212 °F | ASTM D695 | ||
| 185 μm/m-°C @Temperature 100 - 150 °C | 103 μin/in-°F @Temperature 212 - 302 °F | ASTM E831 | |||
| 252 μm/m-°C @Temperature 150 - 200 °C | 140 μin/in-°F @Temperature 302 - 392 °F | ASTM E831 | |||
| Specific Heat Capacity | 0.250 J/g-°C @Temperature 25.0 °C | 0.0598 BTU/lb-°F @Temperature 77.0 °F | DSC | ||
| 0.300 J/g-°C @Temperature 100 °C | 0.0717 BTU/lb-°F @Temperature 212 °F | DSC | |||
| 0.340 J/g-°C @Temperature 150 °C | 0.0813 BTU/lb-°F @Temperature 302 °F | DSC | |||
| 0.380 J/g-°C @Temperature 300 °C | 0.0908 BTU/lb-°F @Temperature 572 °F | DSC | |||
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft2-°F | |||
| Melting Point | 255 - 280 °C | 491 - 536 °F | ASTM D3159 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 °C | 178 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | ASTM D648 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | 30 - 32 % | 30 - 32 % | Limiting Oxygen Index; ASTM D2863 | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 94 % @Thickness 0.0250 mm, Wavelength 400 nm | 94 % @Thickness 0.000984 in, Wavelength 400 nm | |||
| 94 % @Thickness 0.0250 mm, Wavelength 500 nm | 94 % @Thickness 0.000984 in, Wavelength 500 nm | ||||
| 94 % @Thickness 0.0250 mm, Wavelength 600 nm | 94 % @Thickness 0.000984 in, Wavelength 600 nm | ||||
| 95 % @Thickness 0.0250 mm, Wavelength 700 nm | 95 % @Thickness 0.000984 in, Wavelength 700 nm | ||||
| 95 % @Thickness 0.0250 mm, Wavelength 800 nm | 95 % @Thickness 0.000984 in, Wavelength 800 nm | ||||
| UV Transmittance | 91.5 % @Thickness 0.0250 mm, Wavelength 200 nm | 91.5 % @Thickness 0.000984 in, Wavelength 200 nm | |||
| 92 % @Thickness 0.0250 mm, Wavelength 250 nm | 92 % @Thickness 0.000984 in, Wavelength 250 nm | ||||
| 92 % @Thickness 0.0250 mm, Wavelength 300 nm | 92 % @Thickness 0.000984 in, Wavelength 300 nm | ||||
| 93 % @Thickness 0.0250 mm, Wavelength 350 nm | 93 % @Thickness 0.000984 in, Wavelength 350 nm | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 302 - 323 °C | 576 - 613 °F | Cure Temperature | ||
| Descriptive Properties | |||||
| 20% Hydrochloric Acid Transmission, g/100sq in. | <0.02 | ||||
| 50% Sodium Hydroxide Transmission, g/100sq in. | <.02 | ||||
| Acetic Acid Transmission, g/100sq in. | 0.41 | ||||
| Acetone Transmission, g/100sq in. | 0.95 | ||||
| Acetophenone Transmission, g/100sq in. | 0.5 | ||||
| Benzene Transmission, g/100sq in. | 0.64 | ||||
| Carbon Tetrachloride Transmission, g/100sq in. | 0.31 | ||||
| Chemical/Solvent Resistance | Excellent | ||||
| Ethyl Acetate Transmission, g/100sq in. | 0.76 | ||||
| Folding Endurance, # cycles, .18-.20 mm | 10-27 E3 | ||||
| Heat of Combustion J/g | 13700 | ASTM D240 | |||
| Hexane Transmission, g/100sq in. | 0.56 | ||||
| Piperidine Transmission, g/100sq in. | 0.04 | ||||
| Red Fuming Nitric Acid Transmission, g/100sq in. | 7.5-1.4 | ||||
| Salt Spray Resistance on aluminum, Hours | 1000 | ||||
| Sulfuric Acid Transmission, g/100sq in. | 0.00001 | ||||
| Water Transmission, g/100sq in. | 0.4 | ||||
| Weather Resistance | 15 | Years unaffected in Florida Exposure | |||