| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.73 g/cc | 1.73 g/cc | ASTM D792 | ||
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 297 °C | 10 g/10 min @Load 11.0 lb, Temperature 567 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ASTM D638 | ||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 | ||
| Elongation at Break | 425 % | 425 % | ASTM D638 | ||
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.58 @Frequency 1e+6 Hz | 2.58 @Frequency 1e+6 Hz | ASTM D150 | ||
| Dielectric Strength | 150 kV/mm | 3810 kV/in | 0.1 mm; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 267 °C | 513 °F | ASTM D4591 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | DIN 57207 part 6 | ||
| Minimum Service Temperature, Air | -200 °C | -328 °F | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | >= 30 % | >= 30 % | limiting; ASTM D2863 | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | >= 90 % @Wavelength 380 - 780 nm, Thickness 0.100 mm | >= 90 % @Wavelength 380 - 780 nm, Thickness 0.00394 in | film | ||
| Descriptive Properties | |||||
| Flame Rating (110 μm film) | Building Material Class B1 | ||||