- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.67
- 吸水率 [%]: 0.01
- 缺口沖擊強度: 0.25
- 拉伸強度 [MPa]: 29.0
- 斷裂伸長率 [%]: 26.2
- 彎曲強度 [MPa]: 19.0
- 彎曲模量 [MPa]: 1.65
- 硬度: 73.0
- 熱變形溫度 [℃]: 90.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 - 1.87 g/cc | 0.0603 - 0.0676 lb/in3 | Average value: 1.69 g/cc Grade Count:26 |
| Water Absorption | 0.0100 - 0.100 % | 0.0100 - 0.100 % | Average value: 0.0614 % Grade Count:7 |
| Water Absorption at Saturation | 0.100 % | 0.100 % | Average value: 0.100 % Grade Count:11 |
| Particle Size | 28.0 - 80.0 μm | 28.0 - 80.0 μm | Average value: 65.1 μm Grade Count:7 |
| Linear Mold Shrinkage | 0.00200 - 0.0250 cm/cm | 0.00200 - 0.0250 in/in | Average value: 0.0229 cm/cm Grade Count:11 |
| Melt Flow | 1.00 - 550 g/10 min | 1.00 - 550 g/10 min | Average value: 37.5 g/10 min Grade Count:18 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 73.0 - 120 | 73.0 - 120 | Average value: 90.9 Grade Count:14 |
| Hardness, Shore D | 69.0 - 85.0 | 69.0 - 85.0 | Average value: 75.3 Grade Count:14 |
| Tensile Strength, Ultimate | 19.0 - 55.0 MPa | 2760 - 7980 psi | Average value: 47.0 MPa Grade Count:15 |
| Tensile Strength, Yield | 29.0 - 68.9 MPa | 4210 - 10000 psi | Average value: 32.5 MPa Grade Count:15 |
| Elongation at Break | 1.00 - 300 % | 1.00 - 300 % | Average value: 220 % Grade Count:17 |
| Elongation at Yield | 1.00 - 10.0 % | 1.00 - 10.0 % | Average value: 5.04 % Grade Count:12 |
| Modulus of Elasticity | 1.20 - 1.96 GPa | 174 - 284 ksi | Average value: 1.68 GPa Grade Count:16 |
| Flexural Yield Strength | 26.2 - 114 MPa | 3800 - 16500 psi | Average value: 50.1 MPa Grade Count:15 |
| Flexural Modulus | 1.65 - 6.21 GPa | 240 - 900 ksi | Average value: 1.99 GPa Grade Count:15 |
| Izod Impact, Notched | 0.250 J/cm - NB | 0.468 ft-lb/in - NB | Average value: 2.26 J/cm Grade Count:14 |
| 0.640 - 1.22 J/cm @Temperature -40.0 - -40.0 °C | 1.20 - 2.29 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.82 J/cm Grade Count:2 | |
| 0.190 - 2.10 J/cm @Temperature -40.0 - -40.0 °C | 0.356 - 3.93 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.82 J/cm Grade Count:10 | |
| 0.190 - 2.10 J/cm @Thickness 3.20 - 3.20 mm | 0.356 - 3.93 ft-lb/in @Thickness 0.126 - 0.126 in | Average value: 1.82 J/cm Grade Count:10 | |
| Coefficient of Friction | 0.190 - 0.860 | 0.190 - 0.860 | Average value: 0.262 Grade Count:15 |
| Coefficient of Friction, Static | 0.190 - 0.200 | 0.190 - 0.200 | Average value: 0.198 Grade Count:12 |
| Taber Abrasion, mg/1000 Cycles | 5.00 | 5.00 | Average value: 5.00 Grade Count:12 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 - 1.00e+17 ohm-cm | 1.00e+15 - 1.00e+17 ohm-cm | Average value: 4.87e+16 ohm-cm Grade Count:14 |
| Surface Resistance | 1.00e+12 - 1.00e+17 ohm | 1.00e+12 - 1.00e+17 ohm | Average value: 5.25e+16 ohm Grade Count:4 |
| Dielectric Constant | 2.47 - 2.60 | 2.47 - 2.60 | Average value: 2.56 Grade Count:15 |
| Dielectric Strength | 0.551 - 105 kV/mm | 14.0 - 2670 kV/in | Average value: 21.7 kV/mm Grade Count:16 |
| Dissipation Factor | 0.00140 - 0.0140 | 0.00140 - 0.0140 | Average value: 0.00675 Grade Count:3 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Heat of Fusion | 28.0 - 42.0 J/g | 12.0 - 18.1 BTU/lb | Average value: 39.7 J/g Grade Count:10 |
| CTE, linear | 18.0 - 101 μm/m-°C | 10.0 - 56.0 μin/in-°F | Average value: 89.9 μm/m-°C Grade Count:16 |
| 135 - 135 μm/m-°C @Temperature 85.0 - 125 °C | 75.0 - 75.0 μin/in-°F @Temperature 185 - 257 °F | Average value: 135 μm/m-°C Grade Count:2 | |
| Specific Heat Capacity | 0.946 - 0.962 J/g-°C | 0.226 - 0.230 BTU/lb-°F | Average value: 0.959 J/g-°C Grade Count:12 |
| Thermal Conductivity | 0.150 - 0.151 W/m-K | 1.04 - 1.05 BTU-in/hr-ft2-°F | Average value: 0.150 W/m-K Grade Count:4 |
| 0.150 - 0.150 W/m-K @Temperature 40.0 - 40.0 °C | 1.04 - 1.04 BTU-in/hr-ft2-°F @Temperature 104 - 104 °F | Average value: 0.150 W/m-K Grade Count:10 | |
| Melting Point | 225 - 242 °C | 437 - 468 °F | Average value: 237 °C Grade Count:23 |
| Crystallization Temperature | 205 - 222 °C | 401 - 432 °F | Average value: 220 °C Grade Count:10 |
| Maximum Service Temperature, Air | 140 - 150 °C | 284 - 302 °F | Average value: 148 °C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 - 232 °C | 194 - 450 °F | Average value: 102 °C Grade Count:14 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 - 210 °C | 145 - 410 °F | Average value: 73.8 °C Grade Count:16 |
| Brittleness Temperature | -76.0 - 20.0 °C | -105 - 68.0 °F | Average value: -68.0 °C Grade Count:12 |
| Glass Transition Temp, Tg | 85.0 °C | 185 °F | Average value: 85.0 °C Grade Count:10 |
| Decomposition Temperature | 300 - 405 °C | 572 - 761 °F | Average value: 395 °C Grade Count:10 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:17 |
| Oxygen Index | 52.0 - 60.0 % | 52.0 - 60.0 % | Average value: 52.8 % Grade Count:15 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 252 - 282 °C | 486 - 540 °F | Average value: 260 °C Grade Count:3 |