- 密度 [g/cm3]: 1.66
- 吸水率 [%]: 0.01
- 缺口沖擊強度: 0.747
- 斷裂伸長率 [%]: 24.0
- 彎曲強度 [MPa]: 21.0
- 彎曲模量 [MPa]: 1.21
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 - 1.92 g/cc | 0.0600 - 0.0694 lb/in3 | Average value: 1.80 g/cc Grade Count:10 |
| Filler Content | 10.0 - 30.0 % | 10.0 - 30.0 % | Average value: 21.9 % Grade Count:8 |
| Water Absorption | 0.0100 - 0.0200 % | 0.0100 - 0.0200 % | Average value: 0.0140 % Grade Count:5 |
| Linear Mold Shrinkage | 0.00100 - 0.00800 cm/cm | 0.00100 - 0.00800 in/in | Average value: 0.00311 cm/cm Grade Count:9 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00200 - 0.00800 cm/cm | 0.00200 - 0.00800 in/in | Average value: 0.00450 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 21.0 - 75.8 MPa | 3050 - 11000 psi | Average value: 58.5 MPa Grade Count:10 |
| Elongation at Break | 0.550 - 78.0 % | 0.550 - 78.0 % | Average value: 15.4 % Grade Count:10 |
| Modulus of Elasticity | 1.51 - 17.9 GPa | 219 - 2600 ksi | Average value: 8.01 GPa Grade Count:9 |
| Flexural Yield Strength | 24.0 - 96.5 MPa | 3480 - 14000 psi | Average value: 84.7 MPa Grade Count:10 |
| Flexural Modulus | 1.21 - 14.5 GPa | 175 - 2100 ksi | Average value: 6.37 GPa Grade Count:10 |
| Izod Impact, Notched | 0.747 - 6.15 J/cm | 1.40 - 11.5 ft-lb/in | Average value: 3.25 J/cm Grade Count:10 |
| Izod Impact, Unnotched | 2.40 - 13.9 J/cm | 4.50 - 26.0 ft-lb/in | Average value: 9.25 J/cm Grade Count:10 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | Average value: 1.00e+17 ohm-cm Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 24.0 - 80.0 μm/m-°C | 13.3 - 44.4 μin/in-°F | Average value: 52.7 μm/m-°C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 199 °C | 122 - 390 °F | Average value: 132 °C Grade Count:3 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 274 - 335 °C | 525 - 635 °F | Average value: 304 °C Grade Count:8 |
| Mold Temperature | 65.6 - 149 °C | 150 - 300 °F | Average value: 107 °C Grade Count:8 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:8 |