- 密度 [g/cm3]: 1.75
- 缺口沖擊強(qiáng)度: 0.53
- 彎曲模量 [MPa]: 13.93
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in3 | ASTM D 792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D 638 |
| Elongation at Break | 0.70 % | 0.70 % | ASTM D 638 |
| Tensile Modulus | 16.44 GPa | 2384 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 137 MPa | 19900 psi | ASTM D 790 |
| Flexural Modulus | 13.93 GPa | 2020 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C | 0.993 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 2.85 J/cm @Temperature 23.0 °C | 5.34 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 153 °C @Thickness 3.20 mm | 307 °F @Thickness 0.126 in | unannealed; ASTM D 648 |