- 熔體流動速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.938
- 拉伸強度 [MPa]: 20.2
- 彎曲模量 [MPa]: 0.717
- 熱變形溫度 [℃]: 56.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.330 - 0.390 g/cc | 0.0119 - 0.0141 lb/in3 | ASTM D1895 | ||
| Density | 0.938 g/cc | 0.0339 lb/in3 | ASTM D792 | ||
| Particle Mesh Size | 35.0 Mesh | 35.0 Mesh | less than 2%; ASTM D1921 | ||
| ESCR 100% Igepal? | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | F50; ASTM D1693 | ||
| ESCR 10% Igepal? | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | F50; ASTM D1693 | ||
| Melt Flow | 3.50 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 20.2 MPa | 2930 psi | ASTM D638 | ||
| Elongation at Yield | 11.3 % | 11.3 % | (2 in/min); ASTM D638 | ||
| Flexural Modulus | 0.717 GPa | 104 ksi | 1% Secant; ASTM D790B | ||
| Impact Test | 88.1 J @Temperature -40.0 °C | 65.0 ft-lb @Temperature -40.0 °F | 0.144 in.; ARM test | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 56.1 °C | 133 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Pourability | 2.5 - 4 gr/s | ||||
| Process | Rotational Molding | ||||
| Region | Europe/Turkey | ||||