- 熔體流動速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.943
- 拉伸強度 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.943 - 0.951 g/cc @Temperature 23.0 °C | 0.0341 - 0.0344 lb/in3 @Temperature 73.4 °F | |
| 0.945 - 0.953 g/cc @Temperature 20.0 °C | 0.0341 - 0.0344 lb/in3 @Temperature 68.0 °F | ||
| Volatiles | <= 0.035 % | <= 0.035 % | |
| Environmental Stress Crack Resistance | >= 20 hour @Temperature 80.0 °C | >= 20 hour @Temperature 176 °F | Gas component resistance with initial wall stress 2 MPa |
| >= 165 hour @Temperature 80.0 °C | >= 165 hour @Temperature 176 °F | Slow propagation crack resistance, with initial wall stress 4 MPa | |
| Carbon Black Loading | 2.0 - 2.5 % | 2.0 - 2.5 % | |
| Melt Flow | 0.35 - 0.70 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.35 - 0.70 g/10 min @Load 11.0 lb, Temperature 374 °F | ±10% |
| 6.5 - 16 g/10 min @Load 21.6 kg, Temperature 190 °C | 6.5 - 16 g/10 min @Load 47.6 lb, Temperature 374 °F | ||
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 17.0 MPa | >= 2470 psi | |
| Elongation at Break | >= 700 % | >= 700 % | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 200 °C @Time >=1200 sec | 392 °F @Time >=0.333 hour | |