- 密度 [g/cm3]: 0.939
- 拉伸強(qiáng)度 [MPa]: 20.99
- 彎曲模量 [MPa]: 0.5499
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in3 | ASTM D1505 | ||
| Melt Index of Compound | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 67 | 67 | ASTM D2240 | ||
| Tensile Strength, Yield | 20.99 MPa | 3045 psi | 50 mm/min; ASTM D638 | ||
| Elongation at Break | 500 % | 500 % | 50 mm/min; ASTM D638 | ||
| Flexural Modulus | 0.5499 GPa | 79.75 ksi | 1.3 mm/min; ASTM D790 | ||
| Impact | 23 @Temperature -20.0 °C | 23 @Temperature -4.00 °F | J/mm, instrumented impact, rotomolded test sample; ICO R&D1.14 | ||
| Descriptive Properties | |||||
| UV Light Weatherometer Test | 8000 hours | ASTM G26 | |||