- 熔體流動速率 [g/10min]: 0.24
- 密度 [g/cm3]: 0.936
- 缺口沖擊強度: 8.0
- 拉伸強度 [MPa]: 18.0
- 彎曲模量 [MPa]: 0.690
- 熱變形溫度 [℃]: 62.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in3 | ASTM D1505-98 |
| Melt Flow | 0.24 - 0.36 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.24 - 0.36 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238-00 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638-04 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638-02 |
| Elongation at Break | 910 % | 910 % | ASTM D638-02 |
| Elongation at Yield | 14 % | 14 % | ASTM D638-02 |
| Flexural Modulus | 0.690 GPa | 100 ksi | 2% secant; ASTM D790-02 |
| Izod Impact, Notched | 8.00 J/cm | 15.0 ft-lb/in | ASTM D256-03 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 62.0 °C | 144 °F | ASTM D648-97 |