- 密度 [g/cm3]: 0.94
- 拉伸強度 [MPa]: 18.0
- 彎曲模量 [MPa]: 0.75780
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in3 | ASTM D1505 | ||
| Melt Index of Compound | 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.6 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 62 | 62 | ASTM D2240 | ||
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | 50 mm/min; ASTM D638 | ||
| Elongation at Break | 500 % | 500 % | 50 mm/min; ASTM D638 | ||
| Flexural Modulus | 0.75780 GPa | 109.91 ksi | 1.33 mm/min; ASTM D790 | ||
| Impact | 19 @Temperature -20.0 °C | 19 @Temperature -4.00 °F | J/mm, instrumented impact, rotomolded test sample; ICO R&D1.14 | ||
| Descriptive Properties | |||||
| UV Light Weatherometer Test | 8000 hours | ASTM G26 | |||