- 密度 [g/cm3]: 0.935
- 拉伸強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 0.420
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in3 | ASTM D1505 | ||
| ESCR 10% Igepal? | 10 hour | 10 hour | F50; ASTM D1693 | ||
| Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 53 | 53 | ASTM D2240 | ||
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | 50 mm/min; ASTM D638 | ||
| Elongation at Break | 520 % | 520 % | 50 mm/min; ASTM D638 | ||
| Flexural Modulus | 0.420 GPa | 60.9 ksi | 1.3 mm/min; ASTM D790 | ||
| Impact | 17 @Temperature -20.0 °C | 17 @Temperature -4.00 °F | J/mm, instrumented impact, rotomolded test sample; ICO R&D1.14 | ||
| Descriptive Properties | |||||
| UV Light Weatherometer Test | 8000 hours | ASTM G26 | |||