- 熔體流動速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.946
- 缺口沖擊強度: 12.0
- 拉伸強度 [MPa]: 18.0
- 彎曲模量 [MPa]: 0.650
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in3 | ISO 1183 | ||
| Thermal Stress Crack Resistance | >= 1000 hour | >= 1000 hour | ASTM D 1693 | ||
| Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 | ||
| Carbon Black Loading | 2.25 % | 2.25 % | ISO 6964 | ||
| Melt Flow | 0.70 g/10 min @Load 2.16 kg | 0.70 g/10 min @Load 4.76 lb | ISO 1133 | ||
| 2.7 g/10 min @Load 5.00 kg | 2.7 g/10 min @Load 11.0 lb | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 60 | 60 | ISO 868 | ||
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527-2 | ||
| Elongation at Break | >= 600 % | >= 600 % | ISO 527-2 | ||
| Flexural Modulus | 0.650 GPa | 94.3 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | ISO 180 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 126 °C | 259 °F | ISO 3146 | ||
| Vicat Softening Point | 114 °C | 237 °F | ISO 306 | ||
| Descriptive Properties | |||||
| Food Status | This material conforms to both European and American Food contact regulations. | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.