- 密度 [g/cm3]: 0.938
- 拉伸強度 [MPa]: 19.1392
- 彎曲模量 [MPa]: 0.635
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | ASTM D1505 |
| Melt Index of Compound | 5.4 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.4 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 57 | 57 | ASTM D2240 |
| Tensile Strength, Yield | 19.1392 MPa | 2775.91 psi | 2"/min; ASTM D638 |
| Elongation at Break | 350 % | 350 % | 2"/min; ASTM D638 |
| Flexural Modulus | 0.635 GPa | 92.1 ksi | ASTM D790 |
| Impact | 19.6 @Temperature -20.0 °C | 19.6 @Temperature -4.00 °F | J/mm, instrumented impact, rotomolded test sample; ICO R&D1.14 |