- 熔體流動速率 [g/10min]: 5.5
- 密度 [g/cm3]: 0.9355
- 拉伸強度 [MPa]: 16.3
- 彎曲模量 [MPa]: 0.579
- 熱變形溫度 [℃]: 50.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9355 g/cc | 0.03380 lb/in3 | Exxon Method |
| Environmental Stress Crack Resistance | 200 hour | 200 hour | F50, Condition B; ASTM D-1693 |
| Melt Flow | 5.5 g/10 min | 5.5 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 16.3 MPa | 2360 psi | ASTM D638 |
| Elongation at Break | 405 % | 405 % | ASTM D638 |
| Flexural Modulus | 0.579 GPa | 84.0 ksi | ASTM D790 |
| Impact Test | 179 J @Thickness 6.35 mm, Temperature -40.0 °C | 132 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | Impact Strength; Max Force; ARM |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124.8 °C | 256.6 °F | Exxon Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 50.0 °C | 122 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 38.0 °C | 100 °F | ASTM D648 |