- 熔體流動速率 [g/10min]: 3.3
- 密度 [g/cm3]: 0.938
- 拉伸強度 [MPa]: 17.9
- 彎曲模量 [MPa]: 0.668
- 熱變形溫度 [℃]: 52.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | Exxon Method |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50, Condition B; ASTM D1693 |
| Melt Flow | 3.3 g/10 min | 3.3 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D638 |
| Elongation at Break | 765 % | 765 % | ASTM D638 |
| Flexural Modulus | 0.668 GPa | 96.9 ksi | ASTM D790 |
| Impact Test | 237 J @Thickness 6.35 mm, Temperature -40.0 °C | 175 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | Impact Strength; Max Force; ARM |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126.5 °C | 259.7 °F | Exxon Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 52.5 °C | 127 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 °C | 104 °F | ASTM D648 |