- 熔體流動速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.934
- 拉伸強度 [MPa]: 17.9
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | ASTM D1693 |
| Melt Flow | 0.70 g/10 min | 0.70 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 20.7 MPa | 3000 psi | ASTM D628 |
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D638 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.31 @Frequency 1e+6 Hz | 2.31 @Frequency 1e+6 Hz | ASTM D1531 |
| Dissipation Factor | 0.000060 @Frequency 1e+6 Hz | 0.000060 @Frequency 1e+6 Hz | ASTM D1531 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D2240 |