- 熔體流動速率 [g/10min]: 0.32
- 密度 [g/cm3]: 0.939
- 吸水率 [%]: 0.01
- 拉伸強度 [MPa]: 18.0
- 彎曲強度 [MPa]: 26.0
- 彎曲模量 [MPa]: 0.590
- 脆化溫度 [℃]: -100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in3 | Base Density |
| Water Absorption | 0.010 % | 0.010 % | ASTM D570 |
| Environmental Stress Crack Resistance | 1000 hour | 1000 hour | |
| Melt Flow | 0.32 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.32 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength, Ultimate | 26.0 MPa | 3770 psi | ASTM D638 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
| Elongation at Break | 800 % | 800 % | ASTM D638 |
| Flexural Modulus | 0.590 GPa | 85.6 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 128 °C | 262 °F | ASTM D3417 |
| Vicat Softening Point | 120 °C | 248 °F | ASTM D1525 |
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D696 |