- 熔體流動速率 [g/10min]: 4.8
- 密度 [g/cm3]: 0.936
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in3 | ASTM D792 |
| Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58 | 58 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 16.0 MPa | 2320 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 15.0 MPa | 2180 psi | ASTM D882 |
| Film Elongation at Break, MD | 850 % | 850 % | ASTM D882 |
| Film Elongation at Break, TD | 1100 % | 1100 % | ASTM D882 |
| Secant Modulus, MD | 0.280 GPa | 40.6 ksi | ASTM D882 |
| Secant Modulus, TD | 0.310 GPa | 45.0 ksi | ASTM D882 |
| Coefficient of Friction | >= 1.0 | >= 1.0 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 2.00 g/micron | 50.8 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 12.0 g/micron | 305 g/mil | ASTM D1922 |
| Dart Drop | 1.00 g/micron | 25.4 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 119 °C | 246 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.0 % @Thickness 0.0250 mm | 3.0 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 85 % | 85 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |