- 熔體流動速率 [g/10min]: 1.8
- 密度 [g/cm3]: 0.939
- 拉伸強度 [MPa]: 18.0
- 彎曲模量 [MPa]: 0.650
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in3 | ASTM D792 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50, Condition A, ASTM D1693, 100% Igepal |
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59 | 59 | ASTM D2240 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
| Elongation at Break | >= 1000 % | >= 1000 % | ASTM D638 |
| Flexural Modulus | 0.650 GPa | 94.3 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 118 °C | 244 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 215 °C | 338 - 419 °F | |