- 熔體流動速率 [g/10min]: 0.057
- 密度 [g/cm3]: 0.927
- 缺口沖擊強度: 1.15
- 拉伸強度 [MPa]: 17.0
- 彎曲強度 [MPa]: 33.0
- 彎曲模量 [MPa]: 0.590
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 - 0.949 g/cc | 0.0335 - 0.0343 lb/in3 | Average value: 0.935 g/cc Grade Count:19 |
| Water Vapor Transmission | 10.1 - 14.0 g/m2/day | 0.650 - 0.900 g/100 in2/day | Average value: 12.2 g/m2/day Grade Count:3 |
| Thickness | 20.0 - 38.1 microns | 0.787 - 1.50 mil | Average value: 28.3 microns Grade Count:9 |
| Melt Flow | 0.0570 - 30.0 g/10 min | 0.0570 - 30.0 g/10 min | Average value: 7.81 g/10 min Grade Count:19 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 33.0 - 39.0 MPa | 4790 - 5660 psi | Average value: 37.0 MPa Grade Count:3 |
| Film Tensile Strength at Yield, MD | 12.4 - 35.2 MPa | 1800 - 5100 psi | Average value: 18.8 MPa Grade Count:11 |
| Film Tensile Strength at Yield, TD | 14.7 - 29.6 MPa | 2130 - 4300 psi | Average value: 19.5 MPa Grade Count:11 |
| Tensile Strength, Yield | 17.0 - 27.6 MPa | 2470 - 4000 psi | Average value: 20.6 MPa Grade Count:4 |
| Film Elongation at Break, MD | 150 - 600 % | 150 - 600 % | Average value: 451 % Grade Count:15 |
| Film Elongation at Break, TD | 340 - 900 % | 340 - 900 % | Average value: 613 % Grade Count:15 |
| Elongation at Break | 600 - 910 % | 600 - 910 % | Average value: 813 % Grade Count:4 |
| Elongation at Yield | 12.0 - 14.0 % | 12.0 - 14.0 % | Average value: 12.7 % Grade Count:3 |
| Flexural Modulus | 0.590 - 0.810 GPa | 85.6 - 117 ksi | Average value: 0.684 GPa Grade Count:7 |
| Secant Modulus, MD | 0.214 - 0.938 GPa | 31.0 - 136 ksi | Average value: 0.376 GPa Grade Count:10 |
| Secant Modulus, TD | 0.172 - 0.958 GPa | 25.0 - 139 ksi | Average value: 0.421 GPa Grade Count:10 |
| Izod Impact, Notched | 1.15 - 8.00 J/cm | 2.15 - 15.0 ft-lb/in | Average value: 4.92 J/cm Grade Count:3 |
| Coefficient of Friction | 0.380 - 0.500 | 0.380 - 0.500 | Average value: 0.427 Grade Count:3 |
| Elmendorf Tear Strength MD | 14.0 - 165 g | 14.0 - 165 g | Average value: 77.4 g Grade Count:7 |
| Elmendorf Tear Strength TD | 35.0 - 1350 g | 35.0 - 1350 g | Average value: 419 g Grade Count:7 |
| Elmendorf Tear Strength, MD | 0.800 - 3.94 g/micron | 20.3 - 100 g/mil | Average value: 1.83 g/micron Grade Count:9 |
| Elmendorf Tear Strength, TD | 3.94 - 21.0 g/micron | 100 - 533 g/mil | Average value: 13.8 g/micron Grade Count:9 |
| Dart Drop | 1.57 - 5.12 g/micron | 40.0 - 130 g/mil | Average value: 2.60 g/micron Grade Count:5 |
| Dart drop Test | 30.0 - 290 g | 0.0662 - 0.639 lb | Average value: 119 g Grade Count:13 |
| Film Tensile Strength at Break, MD | 24.8 - 76.5 MPa | 3600 - 11100 psi | Average value: 47.1 MPa Grade Count:15 |
| Film Tensile Strength at Break, TD | 17.0 - 66.2 MPa | 2470 - 9600 psi | Average value: 39.4 MPa Grade Count:15 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 116 - 127 °C | 241 - 261 °F | Average value: 123 °C Grade Count:11 |
| Vicat Softening Point | 116 - 124 °C | 241 - 255 °F | Average value: 121 °C Grade Count:6 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.80 - 10.0 % | 4.80 - 10.0 % | Average value: 7.44 % Grade Count:10 |
| Gloss | 40.0 - 90.0 % | 40.0 - 90.0 % | Average value: 67.9 % Grade Count:11 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 220 °C | 68.0 - 428 °F | Average value: 174 °C Grade Count:5 |
| Melt Temperature | 182 - 280 °C | 360 - 536 °F | Average value: 211 °C Grade Count:6 |