- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.934
- 拉伸強度 [MPa]: 19.3
- 彎曲模量 [MPa]: 0.558
- 熱變形溫度 [℃]: 70.0
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in3 | Base Resin; ASTM D1505 |
| ESCR 10% Igepal? | >= 200 hour | >= 200 hour | ARM Method |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 19.3 MPa | 2800 psi | At 50 mm/min; ASTM D683 IV |
| Flexural Modulus | 0.558 GPa | 81.0 ksi | At 2 mm/min; ASTM D790 |
| Dart drop Total Energy | 200.0 J/cm | 0.3746 ft-lb/mil | (-4oF/-20°C); ASTM D3763 |
| Dart Drop | 152 g/micron | 3860 g/mil | Instrumented Falling Weight (-4°F/-20°C); ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |