- 熔體流動速率 [g/10min]: 0.09
- 密度 [g/cm3]: 0.928
- 吸水率 [%]: 0.01
- 缺口沖擊強度: 1.44
- 拉伸強度 [MPa]: 14.0
- 彎曲強度 [MPa]: 9.2
- 彎曲模量 [MPa]: 0.480
- 熱變形溫度 [℃]: 47.0
- 脆化溫度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 - 0.950 g/cc | 0.0335 - 0.0343 lb/in3 | Average value: 0.938 g/cc Grade Count:30 |
| Water Absorption | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:4 |
| Environmental Stress Crack Resistance | 30.0 - 5000 hour | 30.0 - 5000 hour | Average value: 1220 hour Grade Count:6 |
| 110 - 220 hour @Temperature 30.0 - 50.0 °C | 110 - 220 hour @Temperature 86.0 - 122 °F | Average value: 984 hour Grade Count:12 | |
| Melt Flow | 0.0900 - 85.0 g/10 min | 0.0900 - 85.0 g/10 min | Average value: 10.6 g/10 min Grade Count:30 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59.0 - 63.0 | 59.0 - 63.0 | Average value: 61.4 Grade Count:9 |
| Tensile Strength, Ultimate | 9.20 - 33.0 MPa | 1330 - 4790 psi | Average value: 18.9 MPa Grade Count:13 |
| Tensile Strength, Yield | 14.0 - 22.8 MPa | 2030 - 3300 psi | Average value: 18.9 MPa Grade Count:18 |
| Elongation at Break | 16.0 - 1210 % | 16.0 - 1210 % | Average value: 463 % Grade Count:18 |
| Elongation at Yield | 8.00 - 13.0 % | 8.00 - 13.0 % | Average value: 10.2 % Grade Count:6 |
| Modulus of Elasticity | 0.350 - 0.840 GPa | 50.8 - 122 ksi | Average value: 0.648 GPa Grade Count:7 |
| Flexural Modulus | 0.480 - 0.970 GPa | 69.6 - 141 ksi | Average value: 0.767 GPa Grade Count:21 |
| Izod Impact, Notched | 1.44 - 5.60 J/cm | 2.70 - 10.5 ft-lb/in | Average value: 3.77 J/cm Grade Count:3 |
| Charpy Impact, Notched | 0.800 - 0.800 J/cm2 @Temperature -30.0 - -30.0 °C | 3.81 - 3.81 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 0.800 J/cm2 Grade Count:1 |
| Tensile Impact Strength | 130 - 353 kJ/m2 | 61.9 - 168 ft-lb/in2 | Average value: 221 kJ/m2 Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | Average value: 1.00e+15 ohm-cm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 - 500 μm/m-°C @Temperature -20.0 - 100 °C | 50.0 - 278 μin/in-°F @Temperature -4.00 - 212 °F | Average value: 295 μm/m-°C Grade Count:1 |
| Melting Point | 117 - 131 °C | 243 - 268 °F | Average value: 126 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 47.0 - 77.8 °C | 117 - 172 °F | Average value: 54.8 °C Grade Count:14 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.3 - 41.0 °C | 99.1 - 106 °F | Average value: 38.4 °C Grade Count:12 |
| Vicat Softening Point | 62.0 - 124 °C | 144 - 255 °F | Average value: 104 °C Grade Count:14 |
| Brittleness Temperature | -118 - -70.0 °C | -180 - -94.0 °F | Average value: -90.6 °C Grade Count:5 |
| Flammability, UL94 | HB | HB | Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 - 220 °C | 320 - 428 °F | Average value: 198 °C Grade Count:5 |
| Melt Temperature | 170 - 315 °C | 338 - 599 °F | Average value: 231 °C Grade Count:7 |