- 缺口沖擊強(qiáng)度: 0.598
- 彎曲強(qiáng)度 [MPa]: 53.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 53.8 MPa | 7800 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 4.14 GPa | 600 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Izod Impact, Notched | 0.598 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.12 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 204 - 221 °C | 400 - 430 °F | Molding | ||
| Mold Temperature | 26.7 - 54.4 °C | 80.0 - 130 °F | |||
| Descriptive Properties | |||||
| Product Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.