| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 41.4 MPa | 6000 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 4.14 GPa | 600 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.800 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C @Thickness 3.18 mm | 241 °F @Thickness 0.125 in | Annealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 193 - 221 °C | 379 - 430 °F | |||
| Mold Temperature | 26.7 - 54.4 °C | 80.1 - 130 °F | |||
| Descriptive Properties | |||||
| Filler / Reinforcement | Glass Fiber Reinforcement | ||||
| Forms | Pellets | ||||
| Generic Material | HDPE | ||||
| Generic Name | Polyethylene, High Density (HDPE) | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||