- 密度 [g/cm3]: 1.27
- 彎曲模量 [MPa]: 7.05
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.25 % | 2.25 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 6.80 GPa | 986 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 136 MPa | 19700 psi | ISO 178 | ||
| Flexural Modulus | 7.05 GPa | 1020 ksi | ISO 178 | ||
| Charpy Impact, Notched | 2.40 J/cm2 | 11.4 ft-lb/in2 | ISO 179/1eA | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Cavity temperature | ||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 200 - 210 °C | 392 - 410 °F | |||
| Zone 2 | 210 - 220 °C | 410 - 428 °F | |||
| Zone 3 | 220 - 230 °C | 428 - 446 °F | |||
| Zone 4 | 230 - 240 °C | 446 - 464 °F | |||
| Die Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Melt Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Drying Temperature | 90.0 - 100 °C | 194 - 212 °F | |||
| Dry Time | 2.00 hour | 2.00 hour | |||
| Moisture Content | 0.200 % | 0.200 % | Necessary low maximum residual | ||
| Descriptive Properties | |||||
| Longer pre-drying times/storage | Can be stored in standard conditions until processed. | ||||
| Pre-drying | Drying is not normally required with proper storage | ||||