- 熔體流動速率 [g/10min]: 7.0
- 缺口沖擊強度: 0.53
- 拉伸強度 [MPa]: 29.6
- 彎曲模量 [MPa]: 2.07
- 熱變形溫度 [℃]: 102.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 | ||
| Melt Flow | 7.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 7.0 g/10 min @Load 47.6 lb, Temperature 374 °F | Procedure A; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 29.6 MPa | 4290 psi | Type I, 51 mm/min; ASTM D638 | ||
| Elongation at Break | 4.0 % | 4.0 % | Type I, 51 mm/min; ASTM D638 | ||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 | ||
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 0.993 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C @Thickness 3.18 mm | 216 °F @Thickness 0.125 in | Annealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C @Thickness 3.18 mm | 142 °F @Thickness 0.125 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 16.0 - 50.0 °C | 60.8 - 122 °F | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||
| Features | General Purpose | ||||
| Filler / Reinforcement | Glass Fiber Reinforcement | ||||
| Unspecified Filler\Reinfor., 15% Filler by Weight | |||||
| Forms | Pellets | ||||
| Generic Material | HDPE | ||||
| Generic Name | Polyethylene, High Density (HDPE) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | Automotive Applications | ||||
| Construction Applications | |||||
| Consumer Applications | |||||
| General Purpose | |||||
| Industrial Applications | |||||