- 熔體流動速率 [g/10min]: 0.16
- 密度 [g/cm3]: 0.944
- 拉伸強度 [MPa]: 22.1
- 彎曲模量 [MPa]: 0.758
- 脆化溫度 [℃]: -90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.944 g/cc | 0.0341 lb/in3 | ASTM D1505 |
| ESCR 100% Igepal? | >= 1000 hour | >= 1000 hour | Condition A, B, C, F50; ASTM D1693 |
| Melt Flow | 0.16 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.16 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 34.5 MPa | 5000 psi | 2" (50mm) per min, Type IV; ASTM D638 |
| Tensile Strength, Yield | 22.1 MPa | 3200 psi | 2" (50mm) per min, Type IV; ASTM D638 |
| Elongation at Yield | >= 500 % | >= 500 % | Ultimate, 2" (50mm) per min, Type IV; ASTM D638 |
| Flexural Modulus | 0.758 GPa | 110 ksi | ASTM D3350 |
| 0.965 GPa | 140 ksi | ASTM D790 | |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -90.0 °C | <= -130 °F | ASTM D746 |